Professional 2014 T3 Aluminium Solid Round Bar High Strength Easily Be Weld

Professional 2014 T3 Aluminium Solid Round Bar High Strength Easily Be Weld

aluminium round rod

aluminium alloy billet

Place of Origin:

CHINA

Brand Name:

HUANYU

Model Number:

HYRB2014

Contact Us

Request A Quote
Product Details
Elastic (Young's, Tensile) Modulus:
72 GPa
Elongation At Break:
14%
Fatigue Strength:
18000 Psi
Shear Modulus:
27 GPa
Tensile Strength: Ultimate (UTS):
450 MPa
Tensile Strength: Yield (Proof):
280 MPa
Payment & Shipping Terms
Minimum Order Quantity
1 METRIC TON
Price
Negotiable
Packaging Details
PLYWOOD CASE
Delivery Time
40 DAYS
Payment Terms
T/T
Supply Ability
320METRIC TON PER MONTH
RELATED PRODUCTS
Contact Us
86-023-65820299-104
Contact Now
Product Description

Professional 2014 T3 Aluminium Solid Round Bar High Strength Easily Be Weld

 

2014-T3 aluminium solid round bar

is 2014 aluminum in the T3 temper. To achieve this temper, the metal is solution heat-treated, strain hardened, then naturally aged. Aluminum 2014 alloy can be cold worked in the T4 and T3 tempers. Tight bend radii is not recommended for this alloy.

 

Aluminum 2014 Alloy Chemical Composition Limits 
Weight % Si Fe Cu Mn Cr Mg Ni Zn Ti+Zr Al
2014 A 0.50-0.90 0.50 max 3.9-5.0 0.4-1.2 0.10 0.2-0.8 0.1 max 0.25 max 0.20 max Bal

 

Physical Properties

Properties Metric Imperial
Density 2.8 g/cm3 0.1018 lb/in3
Melting point 510°C 950°F

 

Thermal Properties

Properties Conditions
T (ºC) Treatment
Thermal expansion 23 (10-6/ºC) 20-100 -
Thermal conductivity 192 (W/mK) 25 O

 

 

Professional 2014 T3 Aluminium Solid Round Bar High Strength  Easily Be Weld 0Professional 2014 T3 Aluminium Solid Round Bar High Strength  Easily Be Weld 1Professional 2014 T3 Aluminium Solid Round Bar High Strength  Easily Be Weld 2

 