Product Details
Product Name:
2024 Seamless Aluminum Tubing
Ultimate Tensile Strength:
Tensile Yield Strength:
75.8 MPa
Hardness, Brinell:
Elongation At Break (Typical; 1/2 In. (12.7 Mm) Diameter):
21 %
Melting Point:
502 - 638 Degrees C
Annealing Temperature:
413 Degrees C
Solution Temperature:
256 Degrees C
Payment & Shipping Terms
Minimum Order Quantity
Packaging Details
Plywood Case
Delivery Time
21 days
Payment Terms
Supply Ability
45 Metric Tons Per Month
Contact Us
Contact Now
Product Description

High Strength 4 Meters Long Corrosion Resistance 2024 Seamless Aluminum Tubing



2024 is a typical hard aluminum alloy in the aluminum-copper-magnesium series. Its composition is reasonable and the overall performance is better. Many countries produce this alloy, which is used in duralumin. The characteristics of the alloy are: high strength, a certain degree of heat resistance, and can be used as working parts below 150°C. At temperatures higher than 125°C, the strength of 2024 alloy is higher than that of 7075 alloy. The forming properties in the hot state, annealing and new quenching state are better, and the heat treatment strengthening effect is significant, but the heat treatment process is strict. The corrosion resistance is poor, but it can be protected by covering it with pure aluminum; it is easy to produce cracks, but it can also be riveted by special technology. It is widely used in aircraft structures, rivets, truck wheels, propeller components and various other structural parts.




Physical Properties

  Metric English Comments
Density 2.78 g/cc 0.1 lb/in³ AA; Typical

Mechanical Properties
Hardness, Brinell 47 47 AA; Typical; 500 g load; 10 mm ball
Ultimate Tensile Strength 186 MPa 27000 psi AA; Typical
Tensile Yield Strength 75.8 MPa 11000 psi AA; Typical
Elongation at Break 20 % 20 % AA; Typical; 1/16 in. (1.6 mm) Thickness
Elongation at Break 22 % 22 % AA; Typical; 1/2 in. (12.7 mm) Diameter
Modulus of Elasticity 73.1 GPa 10600 ksi AA; Typical; Average of tension and compression. Compression modulus is about 2% greater than tensile modulus.
Ultimate Bearing Strength 345 MPa 50000 psi Edge distance/pin diameter = 2.0
Bearing Yield Strength 131 MPa 19000 psi Edge distance/pin diameter = 2.0
Poisson's Ratio 0.33 0.33  
Fatigue Strength 89.6 MPa 13000 psi AA; 500,000,000 cycles completely reversed stress; RR Moore machine/specimen
Machinability 30 % 30 % 0-100 Scale of Aluminum Alloys
Shear Modulus 28 GPa 4060 ksi  
Shear Strength 124 MPa 18000 psi AA; Typical

Electrical Properties
Electrical Resistivity 3.49e-006 ohm-cm 3.49e-006 ohm-cm AA; Typical at 68 Degrees F

Thermal Properties
CTE, linear 68 Degrees F 23.2 µm/m- Degrees C 12.9 µin/in- Degrees F AA; Typical; Average over 68-212 Degrees F range.
CTE, linear 250 Degrees C 24.7 µm/m- Degrees C 13.7 µin/in- Degrees F Average over the range 20-300 Degrees C
Heat Capacity 0.875 J/g- Degrees C 0.209 BTU/lb- Degrees F  
Thermal Conductivity 193 W/m-K 1340 BTU-in/hr-ft²- Degrees F AA; Typical at 77 Degrees F
Melting Point 502 - 638 Degrees C 935 - 1180 Degrees F AA; Typical range based on typical composition for wrought products 1/4 inch thickness or greater. Eutectic melting is not eliminated by homogenization.
Solidus 502 Degrees C 935 Degrees F AA; Typical
Liquidus 638 Degrees C 1180 Degrees F AA; Typical

Processing Properties
Annealing Temperature 413 Degrees C 775 Degrees F  
Solution Temperature 256 Degrees C 493 Degrees F